Nuclei Engineering for Even Halide Distribution in Stable Perovskite/silicon Tandem Solar Cells

Wide-bandgap (WBG) absorbers in tandem configurations suffer from poor crystallinity and weak texture, which leads to severe mixed halide-cation ion migration and phase segregation during practical operation. We control WBG film growth insensitive to compositions by nucleating the 3C phase before any formation of bromine-rich aggregates and 2H phases. The resultant WBG absorbers show improved crystallinity and strong texture with suppressed nonradiative recombination and enhanced resistance to various aging stresses. Perovskite/silicon tandem solar cells achieve power conversion efficiencies of 29.4% (28.8% assessed by a third party) in a 25–square centimeter active area and 32.5% in a 1–square centimeter active area. These solar cells retained 98.3 and 90% of the original efficiency after 1301 and 800 hours of operation at 25° and 50°C, respectively, at the maximum power point (AM 1.5G illumination, full spectrum, 1-sun) when encapsulated.